Fraises à queue longues, 1 coupe au centre, 37°-39°, type N, queue cylindrique, revêtement AlCrN
|
D
e 8 |
d
h 5 | l1 | l2 | l3 | Dn | Z | Code article | En stock |
|---|---|---|---|---|---|---|---|---|
| 3 | 6 | 57 | 8 | 14 | 2,8 | 3 | S141402X.030 AlCrN | Non |
| 3,5 | 6 | 57 | 8 | 14 | 3,3 | 3 | S141402X.035 AlCrN | Non |
| 4 | 6 | 57 | 11 | 16 | 3,8 | 3 | S141402X.040 AlCrN | Oui |
| 4,5 | 6 | 57 | 11 | 16 | 4,3 | 3 | S141402X.045 AlCrN | Non |
| 5 | 6 | 57 | 13 | 18 | 4,8 | 3 | S141402X.050 AlCrN | Oui |
| 5,5 | 6 | 57 | 13 | 18 | 5,3 | 3 | S141402X.055 AlCrN | Non |
| 6 | 6 | 57 | 13 | 19 | 5,7 | 3 | S141402X.060 AlCrN | Oui |
| 8 | 8 | 63 | 19 | 25 | 7,6 | 3 | S141402X.080 AlCrN | Oui |
| 10 | 10 | 72 | 22 | 30 | 9,5 | 3 | S141402X.100 AlCrN | Oui |
| 12 | 12 | 83 | 26 | 36 | 11,5 | 3 | S141402X.120 AlCrN | Non |
| 14 | 14 | 83 | 26 | 36 | 13,5 | 3 | S141402X.140 AlCrN | Non |
| 16 | 16 | 92 | 32 | 42 | 15,5 | 3 | S141402X.160 AlCrN | Non |
| 18 | 18 | 92 | 32 | 42 | 17,5 | 3 | S141402X.180 AlCrN | Oui |
| 20 | 20 | 104 | 38 | 52 | 19,5 | 3 | S141402X.200 AlCrN | Oui |
Conditions de coupe
Matériaux |
Dureté |
Ap |
Ae |
Vc |
fz(mm/z) Ø 3 |
Ø 4 |
Ø 6 |
Ø 8 |
Ø 10 |
Ø 12 |
Ø 16 |
Ø 20 |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| P.1 | Acier de coupe, acier de construction | ≤ 600 N/mm² | 1xD | 0,1xD | 210 | 0.015 | 0.02 | 0.03 | 0.04 | 0.05 | 0.06 | 0.08 | 0.1 |
| P.3 | Acier à outils faiblement allié | ≤ 1100 N/mm² | 1xD | 0,1xD | 175 | 0.015 | 0.02 | 0.03 | 0.04 | 0.05 | 0.06 | 0.08 | 0.1 |
| P.5 | Acier à outils fortement allié | ≤ 1100 N/mm² | 1xD | 0,1xD | 120 | 0.015 | 0.02 | 0.03 | 0.04 | 0.05 | 0.06 | 0.08 | 0.1 |
| K.1 | Fonte (≤ 240 HB) | ≤ 820 N/mm² | 1xD | 0,1xD | 150 | 0.015 | 0.02 | 0.03 | 0.04 | 0.05 | 0.06 | 0.08 | 0.1 |
| K.2 | Fonte (> 240 HB) | < 800 N/mm² | 1xD | 0,1xD | 110 | 0.015 | 0.02 | 0.03 | 0.04 | 0.05 | 0.06 | 0.08 | 0.1 |
| S.1 | Alliage Cr-Ni | ≤ 1500 N/mm² | 1xD | 0,1xD | 50 | 0.015 | 0.02 | 0.03 | 0.04 | 0.05 | 0.06 | 0.08 | 0.1 |
| S.2 | Titane, alliages de titane | ≤ 1250 N/mm² | 1xD | 0,1xD | 70 | 0.015 | 0.02 | 0.03 | 0.04 | 0.05 | 0.06 | 0.08 | 0.1 |
| H.1 | Acier trempé (< 54 HRC) | ≤ 1920 N/mm² | 1xD | 0,1xD | 120 | 0.015 | 0.02 | 0.03 | 0.04 | 0.05 | 0.06 | 0.08 | 0.1 |
| H.2 | Acier trempé (54 - 60 HRC) | 1920 - 2210 N/mm² | 1xD | 0,1xD | 100 | 0.015 | 0.02 | 0.03 | 0.04 | 0.05 | 0.06 | 0.08 | 0.1 |
Attributs du produit
Queue plaine - DIN 6535 HA.
Application universelle. Convient pour les matériaux jusqu'à la résistance de 900 MPa.
Directions possibles de mouvement
Huile de refroidissement.
Revêtement avec une haute résistance abrasive, avec stabilité et la ténacité à des températures élevées.
Standard de l´entreprise
Angle d'Hélice = 37/39°.
Angle de Pointe = 6°.
Élaboration de la tête
Les matériaux en carbure se caractérisent par une résistance élevée à la compression, une dureté élevée et donc une grande résistance à l'usure, mais aussi une résistance à la flexion et une ténacité limitées.